“Data exchange” service offers individual users metadata transfer in several different formats. Citation formats are offered for transfers in texts as for the transfer into internet pages. Citation formats include permanent links that guarantee access to cited sources. For use are commonly structured metadata schemes : Dublin Core xml and ETUB-MS xml, local adaptation of international ETD-MS scheme intended for use in academic documents.
Export
Janković, Ognjenka
Biokompatibilnost nanostrukturnih biomaterijala na bazi kalcijum aluminata
Dozvoljavate samo preuzimanje i distribuciju dela, ako/dok se pravilno naznačava ime autora, bez ikakvih promena dela i bez prava komercijalnog korišćenja dela. Ova licenca je najstroža CC licenca. Osnovni opis Licence: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/deed.sr_LATN. Sadržaj ugovora u celini: http://creativecommons.org/licenses/by-nc-nd/3.0/rs/legalcode.sr-Latn
Academic metadata
Doktorska disertacija
Medicinske nauke
Univerzitet u Banjoj Luci
Medicinski fakultet
Other Theses Metadata
Biocompatibility of nanostructured biomaterials based on calcium aluminate
143 listova
medicinske nauke - stomatologija / Medical science - Dentistry
Živković, Slavoljub (mentor)
Biokompatibilnost je sposobnost materijala da nakon aplikacije obavlja odreĊenu
funkciju u organizmu ne izazivajući pri tome neţeljeni odgovor tkiva domaćina. Cilj ovog rada je bio da se ispita biokompatibilnost nanostrukturnih biomaterijala na bazi kalcijum aluminata (CA) u komparaciji sa kalcijum silikatom,kalcijum silikat hidroksiapatitom i komercijalnim mineraltrioksid agregatom. Istraţivanje je realizovano u 4 faze: ispitivanje citotoksiĉnosti materijala primjenom MTT testa, ispitivanje genotoksiĉnosti materijala primjenom Komet testa, ispitivanje biokompatibilnosti materijala implantacijom u potkoţno tkivo pacova i ispitivanje biokompatibilnosti materijala nakon direktnog prekrivanja eksponirane pulpe pacova. Prema rezultatima MTT-a samo je CS-HA pokazao citotoksiĉnu aktivnost, dok je ista izostala kod CA i MTA. Komet test je raĊen na istoj ćelijskoj liniji (MRC-5) sa CA i CS-HA cementom. Prilikom Komet testa CA nije ispoljio genotoksiĉni
efekat, procenat oštećenja DNK pri svim primijenjenim koncentracijama je bio na nivou netretiranih kontrolnih ćelija, dok je CS-HA pokazao genotoksiĉni potencijal pri koncentracijama ≥ 12,5 mg/mL. Prilikom in vivo studije potkoţne implantacije na 18 pacova Wistar soja CA je pokazao komparativan rezultat sa CS-HA i MTA kad je u pitanju zapaljenje, uz najbolje organizovanu fibroznu kapsulu oko materijala i blagu narušenost strukture vezivnog tkiva. Prema rezultatima DPP kod većine ispitivanih uzoraka zuba zapaljenje je bilo odsutno ili je konstatovano prisustvo nekoliko raštrkanih upalnih ćelija. Bakterije nisu bile prisutne ni u jednom uzorku. Kod svih primijenjenih materijala je posle 30 dana došlo do formiranja dentinskog mosta. Kalcijum aluminat je indukovao stvaranje najkompletnijeg dentinskog mosta.
Biocompatibility is the ability of the material to perform a certain function in the body after an application without causing an adverse response to the host tissue. The aim of this paper was to examine the biocompatibility of calcium aluminate nanostructured biomaterials (CA) in comparison with calcium silicate, calcium silicate hydroxyapatite and commercial mineraltrioxide aggregate. The research was carried out in 4 phases: testing of cytotoxicity of the material using MTT test, examination of the genotoxicity of the material using the Comet test, testing of the biocompatibility of the material by implantation in the
subcutaneous tissue of the rat and testing of the biocompatibility of the material after direct overlap of the exposed rat pulp. According to MTT results, only CS-HA showed cytotoxic activity, while it was absent in CA and MTA. The comet test was performed on the same cell line (MRC-5) with CA and CS-HA cement. During the Comet test CA did not exhibit a genotoxic effect, the percentage of DNA damage at all applied concentrations was at the level of untreated control cells, while CS-HA showed a genotoxic potential at concentrations of ≥ 12.5 mg / mL. During the in vivo subcutaneous implantation study of 18 rats, Wistar CA CA showed a comparative score with CS-HA and MTA when it comes to inflammation, with the best-organized fibrous capsule around the material and a mildly damaged structure of the connective tissue. According to DPP results, most infections of the tooth test were absent or the presence of several scattered inflammatory cells was observed. Bacteria were not present in any sample. With all the materials used, after 30 days, the dentine bridge was formed. Calcium aluminate induced the creation of the most complete dentine bridge.
biocompatibility, cytotoxicity, genotoxicity,subcutaneous implantation, direct
pulp capping, calcium aluminate.
prema CERIF šifrarniku :
B001
Serbian
Biokompatibilnost je sposobnost materijala da nakon aplikacije obavlja odreĊenu
funkciju u organizmu ne izazivajući pri tome neţeljeni odgovor tkiva domaćina. Cilj ovog rada je bio da se ispita biokompatibilnost nanostrukturnih biomaterijala na bazi kalcijum aluminata (CA) u komparaciji sa kalcijum silikatom,kalcijum silikat hidroksiapatitom i komercijalnim mineraltrioksid agregatom. Istraţivanje je realizovano u 4 faze: ispitivanje citotoksiĉnosti materijala primjenom MTT testa, ispitivanje genotoksiĉnosti materijala primjenom Komet testa, ispitivanje biokompatibilnosti materijala implantacijom u potkoţno tkivo pacova i ispitivanje biokompatibilnosti materijala nakon direktnog prekrivanja eksponirane pulpe pacova. Prema rezultatima MTT-a samo je CS-HA pokazao citotoksiĉnu aktivnost, dok je ista izostala kod CA i MTA. Komet test je raĊen na istoj ćelijskoj liniji (MRC-5) sa CA i CS-HA cementom. Prilikom Komet testa CA nije ispoljio genotoksiĉni
efekat, procenat oštećenja DNK pri svim primijenjenim koncentracijama je bio na nivou netretiranih kontrolnih ćelija, dok je CS-HA pokazao genotoksiĉni potencijal pri koncentracijama ≥ 12,5 mg/mL. Prilikom in vivo studije potkoţne implantacije na 18 pacova Wistar soja CA je pokazao komparativan rezultat sa CS-HA i MTA kad je u pitanju zapaljenje, uz najbolje organizovanu fibroznu kapsulu oko materijala i blagu narušenost strukture vezivnog tkiva. Prema rezultatima DPP kod većine ispitivanih uzoraka zuba zapaljenje je bilo odsutno ili je konstatovano prisustvo nekoliko raštrkanih upalnih ćelija. Bakterije nisu bile prisutne ni u jednom uzorku. Kod svih primijenjenih materijala je posle 30 dana došlo do formiranja dentinskog mosta. Kalcijum aluminat je indukovao stvaranje najkompletnijeg dentinskog mosta.